GP-1860 Pure PTFE Packing is a braided packing made of pure PTFE thin yarns fiber, almost complete chemical inertia, dimensional stability, low friction coefficient to compression, and excellent. Resistance to compression are qualities classifying this packing among the best ones available in the industrial field. It is suitable for all the chemical compounds (excepting cast alkaline metals and the gaseous fluorine), alternative and rotary motions shafts operating at low peripheral speed, rods, pistons valve stems, expansion joints, etc.
The Braided packing impregnated with PTFE are also available
| |
 |
Pressure |
Mpa |
2 |
10 |
20 |
Temperature |
℃ |
<280 |
Linear speed |
M/s |
4 |
2 |
2 |
| PH range |
0~14 |
Size |
3mm ~ 50mm |
GP-1862 PTFE Packing
with Oil Lubricant
Braided by PTFE fiber yarns and treated with a
special inert lubricant .Under a minimum pressure of the stuffing
box, it keeps unchanged in the long run. The low friction
coefficient prevents the surface of the shaft from forming heat even
in the presence of high peripheral speeds. GP-1862 Braided Packing is suitable for high-concentrated chemical products, strongly aggressive and oxidative
Rubber core is also available.
| |
|
Pressure |
Mpa |
2 |
10 |
20 |
Temperature |
℃ |
<280 |
Linear speed |
M/s |
8 |
2 |
2 |
| PH range |
0~14 |
Size |
3mm ~ 50mm |
GP-1863 PTFE
Fiber Packing
with PTFE
Braided with PTFE filament, further impregnated piece by piece with PTFE dispersion. Features flexibility, almost complete chemical inertia, dimensional stability, low friction coefficient to compression, and excellent resistance to compression. Easily qualifies among the best packing available in the industrial field. It is suitable for all the chemical compounds (excepting cast alkaline metals and the gaseous fluorine), alternative and rotary motions shafts operating at high peripheral speed, rod, pistons, valve stems, expansion joints, etc.
| |
|
Pressure |
Mpa |
5 |
15 |
25 |
Temperature |
℃ |
-200~ 280 |
Linear speed |
M/s |
20 |
| PH range |
0~14 |
Size |
3mm ~ 50mm |
GP-1864 PTFE
Fiber Packing
with PTFE and Oil Lubricant
Braided with PTFE filament, further impregnated piece by piece with PTFE dispersion. Features flexibility, almost complete chemical inertia, dimensional stability, low friction coefficient to compression, and excellent resistance to compression. Easily qualifies among the best packing available in the industrial field. It is suitable for all the chemical compounds (excepting cast alkaline metals and the gaseous fluorine), alternative and rotary motions shafts operating at high peripheral speed, rod, pistons, valve stems, expansion joints, etc.
| |
|
Pressure |
Mpa |
2 |
10 |
20 |
Temperature |
℃ |
-200~ 280 |
Linear speed |
M/s |
20 |
| PH range |
0~14 |
Size |
3mm ~ 50mm |
|